GAS
SHIELDED WELDING WIRE:
The product is a
CO2 gas shielded welding wire, which is made of excellent
steel by drawing, straightening and copper coating. It has
various characteristic such as open arc、 slag-free、 good weld ability、 high efficiency、 beautiful bead、 littler spatter. The product has high precision size. It is wounded on Spool.
So that it can be welded automatically or semi-automatically.
Applications：
Used for welding
low carbon steel and low alloy steel structures, especially for
welding of thin plates.
SIZES
AVAILABLE:0.6MM,0.8MM,1.0MM,1.2MM,1.6MM
Chemical
Composition of Deposit Metal（%）
|
C
|
Mn
|
Si
|
S
|
P
|
Cu
|
|
0.06-0.15
|
1.40-1.85
|
0.80-1.15
|
≤0.035
|
≤0.025
|
≤0.50
|
Mechanical
properties of
Deposit Metal:
|
Tensile Strength
MPa(Kgf/mm2)
|
Yield point
MPa(Kgf/mm2
|
Elongation
%
|
Impact
Work
AKV(-29℃)
|
|
|
≥500
|
≥420
|
≥22
|
≥27
|
|
TIG WIRE
Tig wire is a double de-oxidised, copper-coated wire eminently suited for
welding in all positions and under satisfactory conditions will
produce less than 4 ml of Hydrogen per 100g of weld metal. The
thin copper coating minimises corrosion of the wire.
Tig wire can be used for welding unalloyed and low-alloyed steels and
produces welds with excellent x-radiographic qualities. This
wire has a universal application field for thick and thin
materials.
Chemical Composition of Deposit Metal（%）
|
C
|
Mn
|
Si
|
S
|
P
|
Cu
|
|
0.06-0.15
|
1.40-1.85
|
0.80-1.15
|
≤0.035
|
≤0.025
|
≤0.50
|
SUBMERGED
ARC WELDING WIRE:
Submerged arc welding wires are primarily used for welding
of massive plates in the industries of steel structure, pressure
vessel, bridge, heavy-duty machinery and piping and are
characterized by excellent welding performance and mechanical
performance, stable electric arc, easy slag removal, good
welding seam forming and high deposition efficiency.
H08A, H08MnA, H10Mn2, H10MnSi and so on are
available, all size of which can be produced at the request of
customer.
|
GB
|
AWS
|
chemical composition
|
|
C
|
Mn
|
Si
|
S
|
P
|
Cr
|
Ni
|
|
H08A
|
EL8
|
≤0.10
|
0.03～0.55
|
≤0.03
|
≤0.030
|
≤0.030
|
≤0.20
|
≤0.30
|
|
H08C
|
EL8
|
≤0.10
|
0.03～0.55
|
≤0.03
|
≤0.015
|
≤0.015
|
≤0.10
|
≤0.10
|
|
H08E
|
EL8
|
≤0.10
|
0.03～0.55
|
≤0.03
|
≤0.020
|
≤0.020
|
≤0.20
|
≤0.30
|
|
H08MnA
|
EM12K
|
≤0.10
|
0.80～1.10
|
≤0.07
|
≤0.030
|
≤0.030
|
≤0.20
|
≤0.30
|
|
H10Mn2
|
EH14
|
≤0.12
|
1.5～1.9
|
≤0.07
|
≤0.035
|
≤0.035
|
≤0.20
|
≤0.30
|
|
H10MnSi
|
EM13K
|
≤0.14
|
0.80～1.10
|
0.60～0.90
|
≤0.035
|
≤0.035
|
≤0.20
|
≤0.30
|
|